84% retention after 300 cycles
This localized high-concentration electrolyte forms an inorganic-rich, thinner SEI on Ge anodes that survives long-term volume changes without particle fracture.
Li, Yong · Wang, Xiaolei · Jiali, Shao · Xuguang, Liu · Kong, Weijie · Zhang, Zhonghua · Mao, Changming · Li, Zhenjiang · Liu, Jing · Li, Guicun
Journal of Alloys and Compounds 2023
1040 mAh g⁻¹ (0.5 A g⁻¹, 300 cycles)
951 mAh g⁻¹ (1.0 A g⁻¹, 500 cycles)