85.62% after 1400 cycles
An inorganics-rich cathode-electrolyte interface formed in situ from CDP and ADN electrolyte additives suppresses capacity fading of Prussian white cathodes during long-term cycling.
Liu, Xiaowei · Yang, Chao · Xie, Jingjing · Zhang, Youcai · Yan, Hua · Han, Jin · You, Ya
Small 2024